Research Process in Surface Modification Methods of Orthodontic Archwires

1. Nanjing Medical University
2. Institute of Stomatology, School of Stomatology, Nanjing Medical University.

Received:2013-10-28 Revised:2013-12-12 Online:2013-12-25 Published:2014-01-09

摘要/Abstract

摘要： 为了改善正畸弓丝的各项性能以满足临床医师的需求，国内外学者尝试运用多样化的医用金属材料表面处理工艺来实现弓丝的表面改性，以期降低正畸弓丝的摩擦系数以提高临床治疗效率，同时赋予弓丝表面良好的耐腐蚀性、生物相容性以及美学性能。本文对口腔正畸弓丝表面改性工艺的发展以及近年来口腔正畸弓丝表面改性方法的研究进展做一综述。

Abstract: In order to improve various performance of the orthodontic archwire to satisfy the needs of clinicians, the domestic and foreign scholars try diversified surface treatment technologies for metallic biomaterials to realize the archwire surface modification, hoping to reduce the friction coefficient and reach good corrosion resistance, biocompatibility, and aesthetics as well.In this paper, the development of surface modification techniques for orthodontic archwires are reviewed,also including the research progress in surface modification methods for orthodontic archwires.

张昊王林马俊青. 口腔正畸弓丝表面改性技术的研究进展[J]. , 2013, 4(4): 209-213.

参考文献

[参考文献]

[1] 卫敏仲，顾汉卿．医用金属材料表面改性与修饰的研究进展[J]．透析与人工器官，2005，16(1)：32-40.
[2] 朱小双，闫玉华．生物医用金属材料表面改性研究[J]．生物骨科材料与临床研究，2006，3(6)：44-47.
[3] 张宁，强颖怀，张春红，等．氮离子注入生物医用金属材料的表面性能研究[J]．热加工工艺，2007，36(4)：52-52,57.
[4] 张俊彦，卜银忠，王琳，等．在钛合金表面制备生物活性复合薄膜的方法．中国专利：CN103160790A[P]，2013-06-19.
[5] 赵红，林国强，关少轩，等．一种镍钛合金表面氧化钛生物活性涂层的制备方法．中国专利：CN101555597[P]，2009-10-14.
[6] Eisenbarth E, Meyle J, Nachtigall W, et al. Influence of the surface structure of titanium materials on the adhesion on fibroblasts[J]. Biomaterials, 1997, 17 (14):1399-1340.
[7] 孙卫平，周维江．等离子喷涂羟基磷灰石涂层人工股骨柄的研制[J]．中国矫形外科杂志，1992，6 (12)：922-923.
[8] 寇生中，程艳玲，郭燕．磁控溅射法在生物材料表面制备羟基磷灰石涂层的研究现状[J]．材料导报，2006，107-110.
[9] 焦明洁．电化学方法在金属钛表面沉积掺镁/掺锶羟基磷灰石涂层[D]．浙江杭州：浙江大学，2011.
[10] 李敏，李惠东，李惠琪，等．等离子体表面改性技术的发展[J]．金属热处理，2004,29(7)：5-9.
[11] Andrea W, Marc G, Raimund H, et al. The effect of surface treatment and clinical use on friction in NiTi orthodontic wires[J]. Dental Materials, 2005, 21:938–945.
[12] Choi S, Joo HJ, Cheong Y, et al. Effects of self-ligating brackets on the surfaces of stainless steel wires following clinical use: AFM investigation[J]. Journal of Microscopy, 2012, 246(1):53-59.
[13] 王晓萍，孙红英，刘月．齿科常用金属合金的腐蚀及细胞毒性研究进展[J]．口腔生物医学，2012，3(4)：212-214.
[14] 周广宏，丁红燕，戴起勋．新型牙齿正畸丝材料在唾液中的往复滑动摩擦磨损特性研究[J]．摩擦学学报，2007，7(5)：411-415.
[15] 赵丽，何皇冕，戚伟忠，等．聚四氟乙烯膜表面处理研究进展[J]．中国塑料，2011，25(6)：22-25.
[16] HusmannP, Bourauel C, Wessinger M, et al. The frictional behavior of coated guiding archwires[J]. Journal of OrofacialOrthopedics, 2002, 63:199 -211.
[17] Farronato G, Maijer R, Carìa MP, et al. The effect of Teflon coating on the resistance to sliding of orthodontic archwires[J]. Eur J Orthod, 2012, 34 (4):410-417.
[18] DeFranco DJ, Spiller RE Jr, Von Fraunhofer JA. Frictional resistances using Teflon-coated ligatures with various bracket-archwire combinations[J]. The Angle Orthodontist, 1995, 65(1): 63-72.
[19] Krishnana M, Seema S, Kumar AV, et al. Corrosion resistance of surface modified nickel titanium archwires[OL]. http://dx.doi.org/10.2319/021813-140.1.
[20] 邵玶，隋解和，冯雪，等．TiNi合金牙弓丝表面环氧树脂/聚四氟乙烯涂层的组织结构与性能[J]．稀有金属材料与工程，2012，41(5)：822-825.
[21] 谢东，冷永祥，黄楠，等．聚合物表面类金刚石薄膜的制备与应用[J]．功能材料，2008，9(39)：1413-1417.
[22] Kusy RP, Keith O, Whitley JQ, et al. Coefficient of friction characterization of surface-modified polycrystalline alumina[J]. Journal of the American Ceramic Society, 1993, 76: 336-342.
[23] Muguruma T, Iijima M, A. Brantley W. Effects of a diamond-like carbon coating on the frictional properties of orthodontic wires[J]. Angle Orthodontist, 2011, 81(1):141-148.
[24] Ohgoe Y, Kobayashi S, Ozeki K. Reduction effect of nickel ion release on a diamond-like carbon film coated onto an orthodontic archwire[J]. Thin Solid Films, 2006, 497:218-222.
[25] Kobayashi S, Ohgoe Y, Ozeki K, et al. Dissolution effect and cytotoxicity of diamond-like carbon coating on orthodontic archwires[J]. J Mater Sci Mater Med, 2007, 18:2263-2268.
[26] Huang SY, Huang JJ, Kang T, et al. Coating NiTi archwires with diamond-like carbon films: reducing fluoride-induced corrosion and improving frictional properties[J]. J Mater Sci Mater Med, 2013, 24(10):2287-2292.
[27] Burstone CJ. Variable-modulus orthodontics[J].Am J Orthod, 1981, 80(1):1-16.
[28] Prystowsky SD, Allen AM, Smith RW, et al. Allergic contact hypersensitivity to nickel, neomycin, ethylenediamine, and benzocaine[J].Arch Derm, 1979, 115(8):959-962.
[29] Zufall SW, Kennedy KC, Kusy RP. Frictional characteristics of composite orthodontic archwires against stainless steel and ceramic brackets in the passive and active configurations[J]. J Mater Sci Mater Med, 1998, 9(11):611-620.
[30] Zufall SW, Kusy RP. Sliding mechanics of coated composite wires and the development of an engineering model for binding[J]. The Angle orthodontist, 2000, 70(1):34-47.
[31] Redlich M, Katz A, Rapoport L, et al. Improved orthodontic stainless steel wires coated with inorganic fullerene-like nanoparticles of WS2 impregnated in electroless nickel-phosphorous film[J]. Dental Materials, 2008, 24(12):1640-1646.
[32] Katz A, Redlich M, RapoportL, et al. Self-lubricating coatings containing fullerene-like WS2nanoparticlesfor orthodontic wires and other possible medical applications[J]. Tribology Letters, 2006, 21(2):135-139.
[33] Tsabari H. Inorganic fullerene-like nanospheres (IF-WS2)Acute oral toxicity, acute toxic class method in the rat[R]. Israel: Harlan Biotech, 2005.
[34] Haist I. Test for sensitization (Local Lymph Node Assay–LLNA) with inorganic fullerene-like WS2 nanospheres. Germany: BSL Disservice, 2005.
[35] Iijima M, Muguruma T, Brantley W, et al. Effect of coating on properties of esthetic orthodontic nickel-titanium wires[J]. The Angle Orthodontist, 2012, 82(2):319-325.