氧化锌晶须填料对义齿基托树脂力学性能的影响

›› 2013, Vol. 4 ›› Issue (3): 130-133.

氧化锌晶须填料对义齿基托树脂力学性能的影响

张潇雯¹,乔萍丽¹,吴艳芬²,吴凤鸣¹

1. 南京医科大学附属口腔医院修复科
2. 同济大学附属口腔医院

收稿日期:2013-08-30 修回日期:2013-09-09 出版日期:2013-09-25 发布日期:2013-10-22
通讯作者: 吴凤鸣 E-mail:wudent@sina.com

Effect of zinc oxide whiskers on mechanical properties of denture base

Received:2013-08-30 Revised:2013-09-09 Online:2013-09-25 Published:2013-10-22

摘要/Abstract

摘要： 目的：研究添加氧化锌晶须对基托树脂力学性能的影响。方法：将氧化锌晶须按不同的质量百分比加入基托粉中，分为空白对照组、1%、3%、5%、7%等五组。根据ISO标准测试各组的力学性能，并对试样断面进行扫描电镜观察。结果：随着氧化锌晶须用量的增加，复合材料的弯曲强度、弯曲弹性模量、显微维氏硬度呈先升后降的趋势。当氧化锌晶须用量为5%时，以上指标测得值最高，分别为（109.00±2.70）MPa、（3645.30±198.68）MPa、（20.57±0.85）kg/mm2，树脂基托较对照组弯曲强度提高18.29%、弯曲弹性模量提高16.07%、显微维氏硬度提高29.94%。结论：氧化锌晶须填料显著增强了基托树脂的力学性能。

Abstract: Objective：This study intended to investigate the mechanical properties of polymethyl methyacrylate denture base into which zinc oxide whiskers was added. Methods：We conducted the study on five groups divided according to zinc oxide whiskers content which was added to the denture base including control at the rate of 1%, 3%, 5%, and 7%. ISO standard was applied in mechanical tests, and the fractured surfaces of specimens were examined under SEM. Results：Flexural strength, flexural modulus and hardness of composite material increased with the increasing content of zinc oxide whiskers in a limited range. The results showed that the flexural strength, flexural modulus and hardness of composite material rising up to (109.00±2.70) MPa, (3645.30±198.68) MPa, (20.57±0.85) kg/mm2, when the amount of zinc oxide whiskers in the base made up 5% of the total. And the flexural strength of the composites was enhanced by 18.29%, flexural modulus by 16.07%, and hardness by 29.9% compared with that of the control group. Conclusions：Zinc oxide whiskers filler significantly enhanced mechanical properties of denture base.

张潇雯乔萍丽吴艳芬吴凤鸣. 氧化锌晶须填料对义齿基托树脂力学性能的影响[J]. , 2013, 4(3): 130-133.

参考文献

[1]Soygun K, Bolayir G, Boztug A.Mechanical and thermal properties of polyamide versus reinforced PMMA denture base materials[J].J Adv Prosthodont,2013,5(2):153-60.
[2]Ladha K, Shah D.An in-vitro evaluation of the flexural strength of heat-polymerized poly (methyl methacrylate) denture resin reinforced with fibers[J].J Indian Prosthodont Soc,2011,11(4):215-220.
[3]牛丽娜, 陈吉华, 方明, 等.四针状氧化锌晶须对复合树脂抗菌性能的影响[J].中华口腔医学杂志,2009,44(4):240-242.
[4]Hu G, Ma Y, Wang B.Mechanical properties and morphology of nylon 11/tetrapod-shaped zinc oxide whisker composite[J].Mater Sci Eng A,2009,504(1/2):8-12.
[5]Xu X, Chen D, Yi Z, et al.Antimicrobial mechanism based on H2O2 generation at oxygen vacancies in ZnO crystals[J].Langmuir,2013,29(18):5573-5580.
[6]Lin HB, Cao MS, Zhao QL, et al .Mechanical reinforcement and piezoelectric properties of nanocomposites embedded with ZnO nanowhiskers[J].Scr Mater,2008,59(7):780-783.
[7]肖月, 杜滢, 王健平, 等.添加四针状氧化锌晶须抗菌剂对义齿软衬材料抗菌性能的初步研究[J].华西口腔医学杂志,2011,29(4):434-436,441.
[8]陈尔凡,郝春功,Vladlkova T.四脚状氧化锌晶须增强聚丙烯复合材料[J].材料研究学报,2007,21(5):465-470.
[9]Zenga A, Zheng Y, Guo Y, et al.Effect of tetra-needle-shaped zinc oxide whisker (T-ZnOw) on mechanical properties and crystallization behavior of isotactic polypropylene[J].Mater Des,2012,34:691-698.
[10]Wen B, Ji B.Crystallization behaviors and mechanical performance of polypropylene/tetrapod-shaped zinc oxide whisker composites[J].J Appl Polym Sci,2012,124(1):138-144.
[11]Shi J, Wang Y, Liu L, et al.Tensile fracture behaviors of T-ZnOw/polyamide 6 composites[J].Mater Sci Eng A,2009,512(1/2):109-116.